Cr GSGG crystal to provide Q-switched operation of the ruby laser – CRYLINK


CLICK HERE Cr GSGG crystal (Cr doped Gadolinium scandium gallium garnet) is a laser material with high efficiency. An electro-optic shutter element was first utilized to provide Q-switched operation of the ruby laser. Passive Q-switched ruby lasers were achieved with saturable dye absorbers and colored glass (compounds of selenium and cadmium sulfide. Recently the operational characteristics of a dye Q-switch for a pulsed ruby laser was still studied for application in underwater holography. However, the dye Q-switch was limited in durability because of degradation (decomposition) of the dyes and the glass Q-switch was readily damaged. Thus, the tetravalent chromium doped gadolinium scandium gallium garnet Gd3Sc2Ga3O12 (Cr4+: GSGG) passive Q-switch ruby laser-offers for the first time high reliability, durability and high efficiency.


评论

发表评论

此博客中的热门博文

Pockels Cells Crystal

1. Pockels Cells Based on the electro-optic effect , when the applied electric area acts on the Pockels cell crystal ( electro-optic crystal ), the Pockels cell crystal (electro-optic crystal) is like a wave plate whose phase delay is related to the used electric field. The polarization state of the outbound light from the Pockels cell crystal will certainly change so that the strength as well as amplitude of the outbound light from the analyzer are regulated, which is electro-optic inflection, and the modulation tool is called a Pockels cell. 2. Pockels cell crystal The crystals that produce the electro-optical effect are called Pockels cell crystals, that is, electro-optical crystals. They each have their benefits. Presently, the major Pockels cell crystals on the marketplace consist of BBO crystals , DKDP crystals , KTP crystals , as well as LN (LiNbO3) crystals . (1) BBO crystal BBO crystal , additionally called barium metaborate crystal, chemical formula BaB2O4, is an electro-opt
阅读全文
图片
  YCOB nonlinear crystal – Laser Crylink laser crylink Description YCOB crystal is one of the most widely used nonlinear optical crystals. Its nonlinear optical coefficient is equivalent to that of BBO crystal and LBO crystal. The effective frequency multiplication coefficients of the second and third order reach 2, 8 and 1, 4 times of KDP respectively. The YCOB crystal has the following advantages : large aperture, high damage intensity in femtosecond regime,about2000-2500GW/cm2 wide allowable Angle range and allowable temperature range, small dispersion Angle, shorter growth period by Cz method. At the same time, it has stable physical and chemical properties (non-deliquescent) and good machining properties. Therefore, it is considered to have good application prospects of blue-green light and UV band optical frequency multiplier crystal. Feature · Electric resistivity is high · Temperature acceptance is high · Laser induce damage threshold is high · Less anisotropy · Thermal expansi
阅读全文

Nd: YVO4 crystal qualities

图片
Neodymium doped yttrium vanadate (Nd: YVO4) is a kind of laser crystal extensively utilized at present. It has superb efficiency as well as is among the major laser crystals for semiconductor pumped solid state lasers today. Nd: YVO4 crystal is a tetragonal crystal, belonging to the uniaxial crystal system, which is composed of doped ion Nd and also laser matrix YVO4. Compared to another frequently utilized Nd: YAG crystal, Nd: YVO4 has the advantage of higher absorption coefficient. In a specific variety of absorption transmission capacity, the absorption effectiveness of Nd: YVO4 is 5 times that of Nd: YAG, the transmission capacity is 2.4-6.3 times that of Nd: YAG, as well as the peak wavelength of the absorption top is reached at concerning 808nm, which has satisfied the requirements of present high-power laser diodes. The boosted sample of Nd: YVO4 at 1064nm and also 1342nm are bigger, and also the boosted random sample of Nd: YAG at 1064nm have to do with 3 times that of Nd: YAG
阅读全文