RTP Electro-optical Q-Switch crystal datasheet-Laser-crylink

RbTiOPO4(RTP) crystal is a kind of nonlinear optical crystal material with excellent comprehensive properties. RTP is currently the most commonly used type of practical electro-optic crystals with high frequency repetition, high power and narrow pulse width laser Q switching. RTP electro-optical devices are not only used in laser micromachining and laser ranging, but also in major scientific exploration projects because of their excellent comprehensive performance.

RbTiOPO4(RTP)—a crystal with large nonlinear optical coefficient, large electro-optical coefficient, high photoresist damage threshold and stable physical and chemical properties

The growth temperature ranges from 950 °C to 800 °C and the growth period is usually between 45 and 60 days.As RTP is transparent from 0.4 to 3.5 μm, it can be used in multiple types of laser such as Er:YAG laser at 2.94 μm with fairly good efficiency. Bulk absorption measurements at 1.064 μm range from 50 to 150 ppm using Photothermal Common Path Interferometer.

Sales

Sales Mail Address: sales@laser-crylink.com
Company Address:
(1) No.200, Zhaoxian Road, Jiading Zone, Shanghai, China
(2) No.3, Hengda Road, Economic and Technological Development Zone, Nanjing, China
Phone: +86 025-68790685

评论

发表评论

此博客中的热门博文

Pockels Cells Crystal

1. Pockels Cells Based on the electro-optic effect , when the applied electric area acts on the Pockels cell crystal ( electro-optic crystal ), the Pockels cell crystal (electro-optic crystal) is like a wave plate whose phase delay is related to the used electric field. The polarization state of the outbound light from the Pockels cell crystal will certainly change so that the strength as well as amplitude of the outbound light from the analyzer are regulated, which is electro-optic inflection, and the modulation tool is called a Pockels cell. 2. Pockels cell crystal The crystals that produce the electro-optical effect are called Pockels cell crystals, that is, electro-optical crystals. They each have their benefits. Presently, the major Pockels cell crystals on the marketplace consist of BBO crystals , DKDP crystals , KTP crystals , as well as LN (LiNbO3) crystals . (1) BBO crystal BBO crystal , additionally called barium metaborate crystal, chemical formula BaB2O4, is an electro-opt
阅读全文
图片
  YCOB nonlinear crystal – Laser Crylink laser crylink Description YCOB crystal is one of the most widely used nonlinear optical crystals. Its nonlinear optical coefficient is equivalent to that of BBO crystal and LBO crystal. The effective frequency multiplication coefficients of the second and third order reach 2, 8 and 1, 4 times of KDP respectively. The YCOB crystal has the following advantages : large aperture, high damage intensity in femtosecond regime,about2000-2500GW/cm2 wide allowable Angle range and allowable temperature range, small dispersion Angle, shorter growth period by Cz method. At the same time, it has stable physical and chemical properties (non-deliquescent) and good machining properties. Therefore, it is considered to have good application prospects of blue-green light and UV band optical frequency multiplier crystal. Feature · Electric resistivity is high · Temperature acceptance is high · Laser induce damage threshold is high · Less anisotropy · Thermal expansi
阅读全文

Nd: YVO4 crystal qualities

图片
Neodymium doped yttrium vanadate (Nd: YVO4) is a kind of laser crystal extensively utilized at present. It has superb efficiency as well as is among the major laser crystals for semiconductor pumped solid state lasers today. Nd: YVO4 crystal is a tetragonal crystal, belonging to the uniaxial crystal system, which is composed of doped ion Nd and also laser matrix YVO4. Compared to another frequently utilized Nd: YAG crystal, Nd: YVO4 has the advantage of higher absorption coefficient. In a specific variety of absorption transmission capacity, the absorption effectiveness of Nd: YVO4 is 5 times that of Nd: YAG, the transmission capacity is 2.4-6.3 times that of Nd: YAG, as well as the peak wavelength of the absorption top is reached at concerning 808nm, which has satisfied the requirements of present high-power laser diodes. The boosted sample of Nd: YVO4 at 1064nm and also 1342nm are bigger, and also the boosted random sample of Nd: YAG at 1064nm have to do with 3 times that of Nd: YAG
阅读全文